Component Guide

Industry Compliance (continued)
Spec/Approval Requirement Products
AMS-DTL-23053/5
(Class1and3)
Flame-resistant material. Continuous operating temperature range
is-55C(-67F)to135C(275F).
Military Grade
Heat Shrink Label
AMS-DTL-23053/6
(Class1)
Flame-resistant material. Continuous operating temperature range
is-55C(-67F)to135C(275F).
Fluid-Resistant
Heat Shrink Label
SAE-AS81531
(RubTest)
Print shall remain legible after 20 rubs with hard hand pressure. High-Temperature
Marker Plate
SAE-AS5942
(RubTest)
Print shall remain legible after 20 rubs with hard hand pressure. Military Grade Heat
Shrink Label,
Halogen-Free Heat
Shrink Label,
Fluid-Resistant Heat
Shrink Label
MIL-STD-883F
(TestStandard)-
Chemical
Information below
The markings on the component parts shall remain legible when
subjected to the following solvents; these solvents will not cause
deleterious, mechanical or electrical damage, or deterioration of
the material.
See below product
for each chemical test
Chemical Used -
METHOD 2015.13
SOLUTION A
At20C-30Camixtureconsistingofthefollowing:(1)onepart
byvolumeofisopropylalcohol;and(2)threepartsbyvolumeof
mineral spirits.
Military Grade Heat
Shrink Label,
Halogen-Free Heat
Shrink Label,
Fluid-Resistant
Heat Shrink Label
Chemical Used -
METHOD 2015.13
SOLUTION B
A semi-aqueous or non-aqueous based organic solvent like a
terpene or heterocyclic compound.
Military Grade Heat
Shrink Label,
Halogen-Free
Heat Shrink Label
Chemical Used -
METHOD 2015.13
SOLUTION D
At63C-70C,amixtureconsistingofthefollowing:(1)42parts
byvolumeofdeionizedwater;(2)1partbyvolumeofpropylene
glycolmonomethylether;and(3)1partbyvolumeof
monoethanolamine.
Military Grade Heat
Shrink Label,
Halogen-Free Heat
Shrink Label,
Fluid-Resistant
Heat Shrink Label
MIL-STD202G
(TestStandard)-
Chemical
Information below
The markings on the component parts shall remain legible when
subjected to the following solvent; these solvents will not cause
deleterious, mechanical or electrical damage, or deterioration of
the material.
See below product
for each chemical test
Chemical Used -
METHOD 215K
SOLUTIONS A
Amixtureconsistingofthefollowing:(1)onepartbyvolumeof
isopropylalcohol;and(2)threepartsbyvolumeofmineralspirits.
Marker Plate
Halogen-Free
Heat Shrink Label,
Raised Panel Label,
Fluid-Resistant
Heat Shrink Label
Chemical Used -
METHOD 215K
SOLUTIONS C
A terpene defluxer consisting of a minimum of 90% d-limonene
and 10 % surfactant.
Marker Plate
Halogen-Free
Heat Shrink Label,
Raised Panel Label
Chemical Used -
METHOD 215K
SOLUTIONS D
Amixtureconsistingofthefollowing:(1)42partsbyvolumewater;
(2)1partbyvolumeofpropyleneglycolmonomethylether;and
(3)1partbyvolumeofmonoethanolamine.
Marker Plate
Halogen-Free
Heat Shrink Label,
Raised Panel Label,
Fluid-Resistant
Heat Shrink Label
BS6853 1999 Vehicle Category 1A for burning behavior and toxic gas
emissions. Smoke Density Class II
Halogen-Free
Heat Shrink Label
NF F00-608 Class
A and H
Print shall remain legible after 10 rubs after being immersed for
168 hrs. in HCL acid, diesel, NaOH base and 70 hrs. in mineral
spirit. Tensile strength shall be equal to or greater than 14MPa and
elongation shall be 400% or higher.
Fluid-Resistant
Heat Shrink Label
LOCA/MSLB
(IEEE323-2003)
The qualification requirements in this standard, when met,
demonstrate and document the ability of equipment to perform
safetyfunction(s)underapplicableserviceconditions,including
design basis events, reducing the risk of common-cause
equipment failure.
High-Temperature
Marker Plate,
Military Grade Heat Shrink
Label(AMS-DTL-23053/5
[Class1and3]only)