Density: 0.42-0.45 g/cm3 (*) (*) this value is variable
Composition: Recycled Polymer Polystyrene: 100% (*)
This product is free of CFC.
This product is free of asbestos.
This product is free of cyanides.
Hardness: Above 70 Shore D (*)
Thickness: This is variable: 5 mm to 27 mm.
Surface: Mouldings have a film that accepts any high quality acrylic latex paint. Light sanding is
required and make sure surface is dust free before applying paint. We strongly suggest testing a
piece prior to painting all of the mouldings.
Ozone depletion factor: o (CFC free, water blown).
Melting temperature: 170-190^ C
Coefficient of linear thermal expansion: 40-60 . 10-6m/ k m
Chemical properties: Does not deteriorate and resistant to most common solvents and moisture.
Physical properties: Shock and splitting resistant.
Influence of time: Dimensionally stable: will not alter by time.
Influence by humidity: Has no influence on the mechanical properties.
Influence of sound: Polyurethane is acoustically neutral.
Influence of light and sun: RPS not UV-resistant for interior use only.
Testing and Evaluation Results
CLAUSE
REQUIREMENTS
RESULT-REMARK
Flexural
Properties
ASTM D 6109-05, Method A
The maximum load at rupture: 508N
Flexural Strength (Modulus of Rupture): 9:10MPa
(Unexposed specimens, Initial Flexural Strength)
Flexural Secant Modulus at 1% Strain: 692MPa
The Maximum Midspan Deflection: 12.94 mm
Freeze-Thaw
Resistance
ASTM D7032-08, Section 4.7
ASTM D 6109-05 Method A
After 3 cycles Freeze-Thaw test,
Flexural Strength (Modulus of Rupture): 8.79 MPa
Decrease of flexural Strength: 3.4%
Fastener Withdrawal
AST D1761-06a
Specimen of 18 mm thickness, Maximum load: 118N
Specimen of 30 mm thickness, Maximum load: 203N
Tensile Properties
ASTM D638-08
Tensile Strength at Break: 3.43 MPa
Percent Elongation after Break: 0.64%
Modulus of Elasticity: 164MPa
Coating Adhesion
ASTM D3359-08, Method A
Scale: 5A
No peeling or removal
The above report testing complied with the applicable requirements of the following criteria: ASTM D7032-08,
ASTM D1761-06, ASTM D6109-05, ASTM D638-08 and D3359-08