Instructions / Assembly

CROSSQUICK

CODE: CQ001

DESCRIPTION:

CROSSQUICK is a polymer modified cement base underlayment formulated

to create a free flowing liquid mortar that seeks its own level and produces a

smooth, hard, flat surface.

RECOMMENDED

USES:

For use over concrete and wooden floors. Can be used under carpeting, vinyl

sheet goods, ceramic tile, wood flooring, Vinyl Composition Tile, stone and

other materials. This is an underlayment and is not designed as a direct

wearing surface.

DESCRIPTION: •Grey Color

•Strong Bond

•Unmatched Adhesion

PRODUCT CHARACTERISTICS

Compressive strength ASTM C 109

1 day ……………………………………………1,500 psi (10.3 MPa)

7 day ……………………………………………3,800 psi (26.2 MPa)

28 day ………………………………………….5,000 psi (34.5 MPa)

Flexural strength ASTM C348

28 day ………………………………………….900 psi (6.2 MPa)

Flexural strength ASTM C580

7 day ……………….…………………………….1,500 psi (10.3 MPa)

28 day …………………………………………..1,800 psi (12.4 MPa)

Tensile strength ASTM C190

28 day ……………………………………………600 psi (4.1 MPa)

Wet Density ......................................128 lbs./ft3 (2050 kg/m3)

•Ready to Use

•Just add water

•Smooth spread ability

SELF LEVELING UNDERLAYMENT

PAGE 1
SELF LEVELING UNDERLAYMENT CROSSQUICK CODE: CQ001 DESCRIPTION: CROSSQUICK is a polymer modified cement base underlayment formulated to create a free flowing liquid mortar that seeks its own level and produces a smooth, hard, flat surface. RECOMMENDED USES: For use over concrete and wooden floors. Can be used under carpeting, vinyl sheet goods, ceramic tile, wood flooring, Vinyl Composition Tile, stone and other materials. This is an underlayment and is not designed as a direct wearing surface.
PAGE 2
CROSSQUICK SELF LEVELING UNDERLAYMENT CODE: CQ001 GENERAL PRODUCT INFORMATION MIXING POURING Add dry material to approximately ¾ gallon of clean water with ½ gallon of Crossco Acryl –B60. Mix with a paddle mixer attached to a high torque ½” drill (650-1000) rpm for 2-3 minutes. Mix only the amount that can be applied in 15 minutes. For optimum application, the mix temperature should be 60-90° F at time of placement.