Plastic Welder™
Description:
Toughened structural adhesive, after curing, produces superior strength to load-bearing bonds to engineered plastics.
Intended Use:
Bond: PVC, fiberglass, ABS, FRT, PBT, PPO, PCBB, Metton®, Lomod®, Valox®, Noryl®, GTX, Minlon®, epoxy, RIM
urethane, galvanized metal, wood, poorly prepared surfaces, and where outdoor weathering or solvent exposure is
anticipated.
Product
features:
Minimal surface preparation
Room temperature cure
1:1 mix ratio
Rapid fixture in thin set
Non-sagging formula
Typical
Physical
Properties:
Technical data should be considered representative or typical only and should not be used for specification purposes.
Limitations:
Surface
Preparation:
Clean surface by solvent-wiping any deposits of heavy grease, oil, dirt, or other contaminants. Surface can also be
cleaned with industrial cleaning equipment such as vapor phase degreasers or hot aqueous baths. If working with metal,
abrade or roughen the surface to significantly increase the microscopic bond area and optimize the bond strength.
Mixing
Instructions:
---- Proper homogenous mixing of resin and hardener is essential for the curing and development of stated strengths. ----
25 ML DEV-TUBE
1. Squeeze material into a small container the size of an ashtray.
2. Using mixing stick included on Dev-tube handle, vigorously mix components for one (1) minute.
3. Immediately apply to substrate.
35ML/50 ML/250 ML/380 ML/400 ML CARTRIDGES
1. Attach cartridge to Mark V™ [50ml], 380ml, 250ml [15:1 caulk gun], or 400ml dispensing systems [manual or
pneumatic].
2. Open tip.
Impact Resistance ASTM D 950
T-Peel Strength ASTM D 1876
Cured Hardness Shore D ASTM D 2240
Adhesive Tensile Shear ASTM D 1002
Color
Viscosity
Weight
Mixed Viscosity
Mix Ratio by Volume
Mix Ratio by Weight
Mixed Density
Flashpoint
Working Time
Fixture Time
Functional Cure
Full Cure
Service Temperature
T-peel
Impact Resistance
Tensile Elongation
Shore Hardness
Gap-Fill
% Solids by Volume
Adhesive Tensile Lap Shear[ABS]
Adhesive Tensile Lap Shear[GBS]
Adhesive Tensile Lap Shear[Polycarb]
Specific Volume
Straw
Adhesive: 55,000 cps; Acttivator: 50,000 cps
Adhesive: 8.4 lbs./gal.; Activator: 8.00 lbs./gal.
50,000 cps
1:1
1:1
8.20lbs./gal. / .98gm/cc
51°F
4-6 min. @ 72°F,
10-15 min. @ 72°F, 22°C
3/4 - 1 hr.
24 hrs.
-67°F to 250°F
35-40 pli
22 ft.lb./in.[2]
15-25%
78 Shore D
0.125 in.
100
1,300 psi
3,500 psi
1,400 psi
28.1 in[3]/lb.
Cured 7 days @ 75° F
TESTS CONDUCTED
Uncured
Devcon, 30 Endicott Street, Danvers, MA 01923 Tel:[phone] Fax:[phone] www.devcon.com
ITW