Heating Test
热滥用测试
A battery is to be heated in a gravity convection or
circulating air oven. The temperature of the oven is to
be raised at a rate of 5±2℃/min to a temperature of
130±2℃ at which temperature the oven is to remain
for 30 minutes before the test is discontinued.
将标准充电后的电池放在重力对流或循环空气的烘箱
中进行加热，烘箱的温度以 5±2℃/min 的速率上升到
130±2℃后恒温 30 分钟。
No explosion, no fire.
不爆炸，不起火。
Over Charging
Test
过充电测试
After discharged at a constant current of 0.2C5A to the
cutoff voltage, the battery shall be charged at
1.0C/4.6V for 7.0hrs.
0.2C 放电至截止电压后，电池用 1C /4.6V 恒流恒压
充电 7.0h。
No explosion, no fire.
不爆炸，不起火。
Over
Discharge Test
过放电测试
At 23±5℃, discharge to 3.0V with 0.5C current, and
then reverse charge with 1C current for 90min.
在 23±5℃状态下,用 0.5C 电流放电至 3.0V,然后 1C 电
流反向充电 90min
No fire and
no explosion
不起火， 不爆炸
Low Pressure
Test
高空模拟测试
After standard charge ,store for 6h at a absolute
pressure of 11.2KPa, next rest for 2hrs at 25±5℃.
按标准方式满充电池后，在绝对压强为 11.2KPa 下放
置 6h，然后在 25±5℃环境中搁置观察 2hrs。
No leakage, no fire and
no explosion
不漏液， 不起火， 不爆炸
Crush test
挤压测试
Fully charged the battery in accordance with standard
charge condition, the battery is to be crushed between
two flat plates. Continuous to applied force on battery
of 13kN(17.2Mpa),stopped until a pressure reading of
Max is reached on the hydraulic ram 电池按标准充电
条件充满电，放置在两块平面金属板 间，持续施加
13KN（17.2Mpa ）的压力，直到液压 油缸施加的压力
达到最大时停止。
No explosion, no fire.
不爆炸，不起火。