5.2 Environmental Safety Test/
环境安全试验
Items
Conditions and others
Performances
Low Pressure
低气压
The standard charged battery is to be stored in the
vacuum chamber. After close the vacuum chamber,
then reduce the pressure, until the internal pressure is
no more than 11.6kPa, and keep for 6 hours.
充饱电的电池，将其搁置在真空箱中。真空箱密闭
后，逐渐减少其内部压力至不高于 11.6kPa(模拟海
拔 15240m)并保持 6 小时。
The battery should be no leakage, no
venting, no rupture, no fire or no
explosion.
电池应不泄露、不泄气、不破裂、
不起火和不爆炸。
Thermal Shock
温度循环
Battery(standard charged) is repeatedly tested with 10
times heat cycling, which means maintaining the
battery for 6hours at –40℃±2℃ and 72℃±2℃
respectively.
The interval of temperature change is kept in 30mins.
电池充满电后，将电池放入温控箱中，
1）在温度 72℃±2℃的实验箱中保持 6 小时
2）将实验箱温度降为–40℃±2℃，保持 6 小时
3）温度转换时间不大于 30 分钟
4）重复步骤 1）~2），共循环 10 次。
The battery should be no leakage, no
venting, no rupture, no fire or no
explosion.
电池应不泄露、不泄气、不破裂、
不起火和不爆炸。
Vibration
/震动试验
Cells and batteries are firmly secured to the platform
of the vibration machine without
distorting the cells in such a manner as to faithfully
transmit the vibration. The vibration should be a
sinusoidal waveform with a logarithmic sweep
between 7 Hz and 200 Hz and back to 7Hz traversed
in 15 minutes.
This cycle should be repeated 12 times for a total of 3
hours for each of three mutually perpendicular
mounting positions of the cell. One of the directions of
vibration must be perpendicular to the terminal face.
The logarithmic frequency sweep is as follows: from 7
Hz a peak acceleration of 1 gn is maintained until 18
Hz is reached. The amplitude is then maintained at 0.8
mm (1.6 mm total excursion) and the frequency
OCV≥90% initial OCV（open
circuit voltage）
The battery should be no leakage, no
venting, no rupture, no fire or no
explosion.
开路电压不低于初始电压 90%,并
能进行正常的充放电。电池应不泄
露、不泄气、不破裂、不起火和不
爆炸。