3.2.8 HAS/HIT-V threaded rods and HIS-N inserts
244 Hilti, Inc. (US) 1-800-879-8000 | www.hilti.com I en español 1-800-879-5000 I Hilti (Canada) Corp. 1-800-363-4458 I www.hilti.com I Anchor Fastening Technical Guide Ed. 17
3.2.8.1 Material specifications
HIT-Z carbon steel material specications
3/8-, 1/2- and 5/8-in. HIT-Z rods are manufactured from AISI 1038 with a minimum tensile strength of 94.2 ksi (650 MPa) and a
minimum yield strength of 75.3 ksi (520 MPa).
3/4-in. HIT-Z rods are manufactured from either AISI 1038 or 18MnV5 with a minimum tensile strength of 94.2 ksi (650 MPa) and
a minimum yield strength of 75.3 ksi (520 MPa).
HIT-Z rods have a electroplate zinc coating with a minimum thickness of 5 µm.
Carbon steel nuts conform to ASTM A563 and ANSI B18.2.2.
Carbon steel washers conform to ASTM F844.
HIT-Z-R stainless steel material specications
HIT-Z-R rods are manufactured from AISI Type 316 stainless steel minimum tensile strength of 94.2 ksi (650 MPa) and a
minimum yield strength of 75.3 ksi (520 MPa).
Stainless steel nuts conform with ASTM F594 and ANSI B18.2.2.
Stainless steel washers are manufactured from AISI Type 316 stainless steel and conform to ASTM A240.
HIT-V carbon steel rod specications
Carbon Steel conforms to ultimate strength of ASTM A307 Grade A of 60,000 psi (414 MPa )but do not meet the minimum
elongation ductility requirement.
HIT-V nuts conform to SAE J995 Grade 5.
HIT-V washers conform to ASTM F594 and ANSI B18.2.2
HIT-V rod, nut and washer have an electroplated zinc coating conforming to ASTM B633, SC 1
HAS-E carbon steel threaded rod specications
Carbon steel rods conform to ISO 898 class 5.8 with a minimum tensile strength of 72.5 ksi (500 MPa) and a minimum yield
strength of 58 ksi (400 MPa) but do not meet the minimum elongation ductility requirement.
HAS-E nuts conform to SAE J995 Grade 5.
HAS-E washers conform to ASTM F844, HV, and ANSI B18.22.1 Type A Plain.
HAS-E rod, nut and washer have an electroplated zinc coating conforming to ASTM B633, SC 1.
HAS-E-B high strength threaded rod specications
Carbon steel rods manufactured from ASTM A193, Grade B7, with a minimum tensile strength of 125 ksi (862 MPa) and
a minimum yield strength of 105 ksi (724 MPa).
HAS-E-B nuts conform to ASTM A 194, Grade 2H, Heavy.
HAS-E-B washers conform to ASTM F844, HV, and ANSI B18.22.1 Type A Plain.
HAS-E-B rods, nuts and washers, except the 7/8-in. diameter, have an electroplated zinc coating conforming to
ASTM B633, SC1.
HAS-E-B HDG rods, nuts and washers are hot-dip galvanized in accordance with ASTM A153.
HAS-R 304 stainless steel
3/8-, 1/2- and 5/8-in. rods manufactured from AISI Type 304 stainless steel with a minimum tensile strength of
100 ksi (689 MPa) and a minimum yield strength of 65 ksi (448 MPa).
3/4-, 1- and 1 1/4-in. rods are manufactured from AISI Type 304 stainless steel conforming to ASTM F593 Condition CW
or cold worked.
AISI Type 304 stainless steel nuts conform to ASTM F594.
AISI Type 304 stainless steel washers conform to ASTM A240 and ANSI B18.22.1 Type A Plain.
HAS-R 316 stainless steel
3/8-, 1/2- and 5/8-in. rods manufactured from AISI Type 316 stainless steel with a minimum tensile strength of
100 ksi (689 MPa) and a minimum yield strength of 65 ksi (448 MPa).
3/4-, 1- and 1 1/4-in. rods are manufactured from AISI Type 316 stainless steel conforming to ASTM F593 Condition CW.
AISI Type 316 stainless steel nuts conform to ASTM F594.
AISI Type 316 stainless steel washers conform to ASTM A240 and ANSI B18.22.1 Type A Plain.
HIS-N and HIS-RN internally threaded insert specications
3/8-in. HIS-N is manufactured from 11MnPb30+C carbon steel conforming to DIN 10277-3 with a minimum tensile strength
of 71.1 ksi (490 MPa) and a minimum yield strength of 59.5 ksi (410 MPa).
1/2-, 5/8- and 3/4-in. HIS-N is manufactured from 11MnPb30+C carbon steel conforming to DIN 10277-3 with a minimum
tensile strength of 66.7 ksi (460 MPa) and a minimum yield strength of 54.4 ksi (375 MPa).
HIS-RN is manufactured from X5CrNiMo17+12+2+2 stainless steel conforming to DIN EN 10088-3 with a minimum tensile
strength of 101.5 ksi (700 MPa) and a minimum yield strength of 50.8 ksi (350 MPa).