Hysol® Product E-60NC
formerly Durabond E-60NC
Industrial Version, August 2001
PRODUCT DESCRIPTION
LOCTITE
®
Hysol
®
Product E-60NC is a flowable, industrial
grade epoxy potting compound with extended work life. Once
mixed, the two-part epoxy cures at room temperature to form a
rigid, black encapsulant that is non-corrosive to metallic
components on PC Boards and electronic assemblies. The
fully cured epoxy provides excellent environmental and
chemical resistance, and acts as an electrical insulator.
TYPICAL APPLICATIONS
Designed for bonding, potting and encapsulating electrical
components which are sensitive to corrosion. Used in
electronic applications, for component attachment to boards,
housing assembly and potting.
PROPERTIES OF UNCURED MATERIAL
Resin
Typical
Value Range
Chemical Type Epoxy
Appearance Black liquid
Specific Gravity @ 25°C 1.10 1.0 to 1.2
Viscosity @ 25°C, mPa.s (cP)
6,200 5,200 to 7,200
Flash Point (TCC), °C (°F)
>93 (>200)
Hardener
Typical
Value Range
Chemical Type Amine
Appearance Pale yellow liquid
Specific Gravity @ 25°C 1.00 0.9 to 1.1
Viscosity @ 25°C, mPa.s (cP)
13,000 12,000 to 14,000
Flash Point (TCC), °C (°F)
>93 (>200)
Mixture
Typical Value
Appearance Black Opaque
Specific Gravity @ 25°C 1.05
Mix Ratio (R:H) by Weight 100 to 91
by Volume 1 to 1
TYPICAL CURING PERFORMANCE
Cure speed
The graph below shows the shear strength developed over
time on abraded, acid etched aluminum lap shears with an
average bondline gap of 3 to 9 mils and tested according to
ASTM D-1002.
Cure Time, Hours @25°C
5min 10min 30min 1hr 3hr 6hr 24hr 72hr0
25
50
75
100
% of Full Strength on Aluminum
1week 1month
Curing Properties
(@ 25°C unless noted)
Typical Value
Working Life, minutes 60
Tack Free time, minutes 180
TYPICAL PROPERTIES OF CURED MATERIAL
(@ 25°C unless noted)
Physical Properties
Typical Value
Dielectric Strength, Volts/Mil 550
Tensile Strength ASTM D638, psi 6,800
Tensile Elongation ASTM D-638, % 8
Hardness ASTM D-1706, Shore D 85
Glass Transition Temperature, Tg, °C
55
PERFORMANCE OF CURED MATERIAL
Shear Strength vs Substrate
(Substrates cured for 5 days @ 22°C)
Substrate Typical Value
Lapshear N/mm
2
(psi)
Grit-Blasted Steel 18.1 2630
Aluminum (Abraded/Acid Etched, 3 to 9 mil gap) 21.4 3110
Aluminum (Anodized) 7.9 1150
Stainless Steel 7.8 1130
Polycarbonate 5.9 850
Nylon 1.3 190
Wood (Fir) 11.1 1610
Block Shear N/mm
2
(psi)
PVC 4.6 670
ABS 6.5 940
Epoxy 14.8 2140
Acrylic 1.2 180
Glass 13.9 2020
TYPICAL ENVIRONMENTAL RESISTANCE
Hot Strength
Test procedure : ASTM D-1002
Substrate: Abraded, acid etched aluminum
Bondline gap, mils: 3 to 9
Cure procedure:
12 hours at 65°C & 4 hours at 22°C
Tested at temperature.
0
25
50
75
100
% RT Strength
Temperature, °C
15010050