Soldering Process
The implementation of the RoHS directive has resulted in the selection of SnAuCu (SAC) alloys or SnCu alloys as a primary solder.
Thishasincreasedtheliquidustemperaturefrom183°CforSnPbeutecticalloyto217–221°Cforthenewalloys.Asaresult,the
heatstresstothecomponents,eveninwavesoldering,hasincreasedconsiderablyduetohigherpre-heatandwavetemperatures.
Polypropylenecapacitorsareespeciallysensitivetoheat(themeltingpointofpolypropyleneis160–170°C).Wavesolderingcan
bedestructive,especiallyformechanicallysmallpolypropylenecapacitors(withleadspacingof5–15mm).Greatcaremustbe
takenduringsoldering.TherecommendedsolderprolesfromKEMETshouldbeused.ConsultKEMETwithanyquestions.In
general,thewavesolderingcurvefromIECPublication61760-1Edition2servesasasolidguidelineforsuccessfulsoldering.
See Figure 1.
Reowsolderingisnotrecommendedforthrough-holelmcapacitors.Exposingcapacitorstoasolderingproleinexcessofthe
recommended limits may result in degradation or permanent damage to the capacitors.
Do not place the polypropylene capacitor through an adhesive curing oven to cure resin for surface-mount components. Insert
through-holepartsaftercuringthesurfacemountparts.ConsultKEMETtodiscusstheactualtemperatureproleintheoven,if
through-hole components must pass through the adhesive curing process. A maximum of two soldering cycles is recommended.
Allowtimeforthecapacitorsurfacetemperaturetoreturntoanormaltemperaturebeforethesecondsolderingcycle.
Manual Soldering Recommendations
Following is the recommendation for manual
soldering with a soldering iron.
Solderingirontiptemperatureshouldbesetat
350°C(+10°Cmaximum),withthesoldering
duration not to exceed more than 3 seconds.
Recommended Soldering Temperature
0
50
100
150
200
250
300
350
400
0 1 2 3 4 5 6 7 8
Soldering Time (seconds)
Soldering Iron Bit Temperature (°C)
Wave Soldering Recommendations
0
50
100
150
200
250
300
0
40
80
120
160
200
240
Temperature (°C)
Time (s)
ca 2°C/second
ca 3.5°C/second typical
ca 5°C/second
Cooling
2 +3 seconds maximum
115 °C max
T
preheat
∆T < 150°C
100 °C
Preheating
Typical
First wave
Second wave
260°C