XRF SCREENING AND CHEMICAL CONFIRMATION TEST REPORT
NUMBER: SZHH00425771
TESTS CONDUCTED
PAGE 27 OF 42
Intertek Testing Services Shenzhen Ltd.-TFH Division
7/F., ShekouTechnology Main Building, Industrial 7th Road,Shekou,Shenzhen, China
Tel: [phone] Fax: [phone] Postcode: 518067
Attention is drawn to the terms and conditions printed overleaf.
POSITIVE = A POSITIVE TEST RESULT INDICATED THE PRESENCE OF Cr(VI) AT THE TIME
OF TESTING, EQUAL TO OR GREATER THAN THRESHOLD OF 1 mg/kg FOR SPOT
TEST PROCEDURE OR 0.02 mg/kg FOR BOILING-WATER-EXTRACTION
PROCEDURES WITH A SAMPLE SURFACE AREA OF 50cm2 USED. HOWEVER, IT
SHALL NOT BE INTERPRETED AS THE Cr(VI) CONCENTRATION IN THE COATING
LAYER OF THE SAMPLE AND SHOULD NOT BE USED AS A METHOD DETECTION
LIMIT FOR THIS QUALITATIVE TEST.
NEGATIVE = A NEGATIVE TEST RESULT INDICATED ABOVE POSITIVE OBSERVATION WAS NOT
FOUND AT THE TIME OF TESTING. WHEN THE SPOT-TEST SHOWED A NEGATIVE
RESULT, THE BOILING-WATER-EXTRACTION PROCEDURE SHALL BE USED TO
VERIFY THE RESULT.
#1 = AS CLAIMED BY THE DECLARATION SUBMITTED BY THE APPLICANT, THE LEAD
CONTENT OF THE COMPONENT IS COMING FROM COPPER ALLOY ONLY. ACCORDING
TO EU RoHS DIRECTIVE (2002/95/EC)AND ITS AMENDMENTS, LEAD AS AN
ALLOYING ELEMENT IN COPPER ALLOY CAN BE CONTAINING UP TO 4% (40,000
ppm) LEAD BY WEIGHT.
#2 = EXCEEDED UPPER SCREENING LIMIT, AS CLAIMED BY THE DECLARATION
SUBMITTED BY THE APPLICANT, MERCURY IN COMPACT FLUORESCENT LAMPS NOT
EXCEEDING 5mg PER LAMP ACCORDING TO EU RoHS DIRECTIVE (2002/95/EC)
AND ITS AMENDMENTS, MERCURY IN COMPACT FLUORESCENT LAMPS NOT
EXCEEDING 5mg PER LAMP CAN BE EXEMPTED.
#3 = AS CLAIMED BY THE DECLARATION SUBMITTED BY THE APPLICANT, THE LEAD
CONTENT OF THE COMPONENT IS COMING FROM THE CONSTITUENT OF GLASS
USED IN ELECTRONIC COMPONENT ONLY. ACCORDING TO EU RoHS DIRECTIVE
(2002/95/EC) AND ITS AMENDMENTS, LEAD IN GLASS OF THIS COMPONENT CAN
BE EXEMPTED.
#4 = AS CLAIMED BY THE DECLARATION SUBMITTED BY THE APPLICANT, THE LEAD
CONTENT OF THE COMPONENT IS COMING FROM THE CONSTITUENT OF HIGH
MELTING TEMPERATURE TYPE SOLDERS (i.e. LEAD BASED ALLOYS CONTAINING
85% BY WEIGHT OR MORE LEAD) ONLY. ACCORDING TO EU RoHS DIRECTIVE
(2002/95/EC) AND ITS AMENDMENTS, LEAD IN HIGH MELTING TEMPERATURE
TYPE SOLDERS OF THIS COMPONENT CAN BE EXEMPTED.
************************************************************************************