Data Sheet

Global Office Locations www.polymaker.com
Shanghai ∙ New York ∙ Utrecht ∙ Tokyo [e-mail]
Technical Data Sheet
Polymaker PC-Max™ is an advanced polycarbonate based filament designed specifically for desktop FDM/FFF 3D
printing. In addition to high printing quality, great mechanical strength and heat resistance, Polymaker PC-Max™
offers excellent impact strength and fracture toughness, making it the ideal choice for engineering applications.
Physical Properties
Property
Testing Method
Typical Value
Density (g/cm
3
at 21.5 ° C)
ASTM D792
(ISO 1183, GB/T 1033)
1.18 - 1.20
Glass transition temperature (° C)
DSC, 10 °C/min
113℃
Softening temperature of filament
(for 1.75 mm; ° C)
Custom method
127 - 130
Melt index (g/10 min)
300 °C, 1.2 kg
23 - 26
Moisture content
1
(%)
Thermogravimetric
≤ 0.1%
Odor
/
Almost odorless
Solubility
/
Insoluble in water
Note:
1. For newly opened filaments; filaments may absorb higher levels of moisture during use.
Mechanical Properties
1
Property
Testing Method
Typical Value
Young’s modulus (MPa)
ASTM D638
(ISO 527, GB/T 1040)
2048 ± 66
Tensile strength (MPa)
ASTM D638
(ISO527, GB/T 1040)
59.7 ± 1.8
Elongation at break (%)
ASTM D638
(ISO527, GB/T 1040)
12.24 ± 1.44
Bending modulus (MPa)
ASTM D790
(ISO 178, GB/T 9341)
2044 ± 55
Bending strength (MPa)
ASTM D790
(ISO 178, GB/T 9341)
94.1 ± 0.9
Impact strength (kJ/m
2
)
ASTM D256
(ISO 179, GB/T 1043)
25.1 ± 1.9
Note:
1. All testing specimens were printed using a FlashForge Creator Pro under the following conditions:
Printing temperature = 255 °C, printing speed = 60 mm/s, number of shells = 2, and 100% infill.