Specifications

2.4GHz 3216 Chip Antenna: RANT3216F245C01
_
Reliability Table
Test Item
Procedure
Requirements
Ceramic Type
Remark
(Reference)
Electrical
Characterization
Fulfill the electrical
specification
User Spec.
Thermal
Shock
1. Preconditioning:
50 ± 10℃ / 1 hr , then keep for 24 ± 1 hrs at room temp.
2. Initial measure: Spec: refer Initialspec.
3. Rapid change of temperature test:
-30℃ to +85℃; 100 cycles;
15 minutes at Lower category temperature;
15 minutes at Upper category temperature.
No Visible Damage.
Fulfill the electrical
specification.
MIL-STD-202
107
Temperature
Cycling
1. Initial measure: Spec: refer Initialspec.
2. 100 Cycles (-30℃ to +85℃), Soak Mode=1 (2 Cycle/hours).
3. Measurement at 24 ± 2Hours after test condition.
No Visible Damage.
Fulfill the electrical
specification.
JESD22
JA104
High Temperature
Exposure
1. Initial measure: Spec: refer Initialspec.
2. Unpowered; 500hours @ T=+85℃.
3. Measurement at 24 ± 2 hours after test.
No Visible Damage.
Fulfill the electrical
specification.
MIL-STD-202
108
Low Temperature
Storage
1. Initial measure: Spec: refer Initialspec.
2. Unpowered: 500hours @ T= -30℃.
3. Measurement at 24 ± 2 hours after test.
No Visible Damage.
Fulfill the electrical
specification.
MIL-STD-202
108
Solderability
(SMD Bottom Side)
Dipping method:
a. Temperature: 235 ± 5°C
b. Dipping time: 3 ± 0.5s
The solder should cover
over 95% of the critical
area of bottom side.
IEC 60384-21/22
4.10
Soldering Heat
Resistance
(RSH)
Preheating temperature: 150 ± 10°C.
Preheating time: 1~2 min.
Solder temperature: 260 ± 5°C.
Dipping time: 5 ± 0.5s
No Visible Damage.
IEC 60384-21/22
4.10
Vibration
5g's for 20 min., 12 cycles each of 3 orientations
Note: Use 8"X5" PCB .031" thick 7 secure points on, one long
side and 2 secure points at corners of opposite sides. Parts
mounted within 2" from any secure point. Test from 10-2000
Hz.
No Visible Damage.
MIL-STD-202
Method 204
Mechanical
Shock
Three shocks in each direction shall be applied along the three
mutually perpendicular axes of the test specimen (18 shocks)
Peak value: 1,500g’s
Duration: 0.5ms
Velocity change: 15.4 ft/s
Waveform: Half-sine
No Visible Damage.
MIL-STD-202
Method 213
Humidity
Bias
1. Humidity: 85% R.H., Temperature: 85 ± 2 °C.
2. Time: 500 ± 24 hours.
3. Measurement at 24 ± 2hrs after test condition.
No Visible Damage.
Fulfill the electrical
specification.
MIL-STD-202
Method 106