SECONDARY HEAT EXCHANGER 316L STAINLESS STEEL
(CONDENSING MODELS ONLY)
The secondary condensing heat exchanger is made of high-quality 316L stainless steel. This is where the rest of the heat
transfer occurs. Due to the lower temperature acidic condensation occurs, and stainless steel is required in order to avoid
corrosion.
For condensing heat exchangers, it is more suitable to use 316L stainless steel because of the extreme environment (heat,
acidic condensation, chloride) that the material is subjected to.
PRIMARY HEAT
EXCHANGER:
COPPER VS.
STAINLESS STEEL
• Heat transfers 25 times more readily
through copper than stainless steel.
Consequently, for the same amount
of heat transfer, stainless steel heat
exchangers need to be larger than
copper heat exchangers, leading to a
larger pressure loss.
• At higher temperatures, it is the nature
of stainless steel to become prone
to a number of problems not usually
experienced at room temperature. It is
vulnerable to pitting corrosion and stress
corrosion cracking (SCC).
• Stainless steel is NOT better for
durability because it is harder.
Hardness causes the material to
become brittle. Stainless steel will
crack after numerous cycles of
thermal expansion/contraction,
especially with chloride in the
water. Copper heat exchangers
are less brittle and better suited
for expansion/contraction without
cracking.
• In a dual heat exchanger design,
corrosion is not a big concern in
the non-condensing primary heat
exchanger because no condensation
forms on the exterior of the pipes.
Stainless steel is unnecessary for this
stage.