www.litokol.it

DESCRIPTION

Part A consists of a mixture of epoxy resin, inert substances based

on glass beads with a fine particle size and components of organic

origin. Part B consists of a mixture of amine-based hardeners.

The main features of the product are:

● Translucent color that allows light refraction

● Smooth finish thanks to the fine particle size of the glass beads

● Extremely easy application and cleaning with clean potable

water

● High mechanical strength

● Water proof

● Total absence of cracks or crazing after hardening

● Excellent chemical resistance

FIELDS OF APPLICATION

Starlike

Crystal’s special translucent coloring allows the product

applied in the joints to “absorb” the color of the adjacent

transparent glass tiles. If backlit is desired the best results are

achieved if the mosaic is applied to transparent substrate such as

glass and Plexiglas, possibly backlit. In this case, the mosaic tiles

must be glued using a suitable transparent adhesive.

In the case of traditional substrate such as cement plasters,

backerboard, paneling, sheet rock, etc. the mosaic tiles must be

bonded using Litokol’ s Hyperflex K100 white adhesive, a class

C2TES2 cement adhesive or Litoelastic, a two-component reactive

adhesive class R2T depending on the type of substrate. Please

read the relative technical data sheets for correct use.

Thanks to the feature of Starlike

Crystal it is possible to get a

glass mosaic surfaces with effects of considerable value and visual

impact such as:

● Creating backlit interior wall. Backlit coatings of bars or public

places.

● Floors and walls in bathrooms, kitchens, showers etc.

● Furnishing surfaces such as columns, tables etc.

Starlike

Crystal can also be used to grout artistic surfaces, i.e.

compositions made up of mosaic tile of murals, blends or patterns

which are rich color, nuances and shadows. If the grouting of

these are done with traditional colored materials, the appearance

of the art work represented is compromised, because the traditional

colored grout creates a discontinuity of color between the mosaic

tiles. Conversely, using Starlike

Crystal, thanks to its semi-

transparency, the art work retains the original nuances of the

composition, creating a “neutral”, colorless grouting that does not

interfere with the image, it remains a neutral effect blends into the

the tile work.

PRELIMINARY CHECKS AND PREPARATION OF JOINTS

Make sure that the adhesive used for bonding the mosaic is

completely dry and hardened. The joints must be completely DRY,

CLEAN, FREE OF DUST and EMPTY for the entire thickness of the

mosaic tile to ensure the translucent effect of the product. If after

initial application and cleaning there is a need to apply more grout

those areas must be fully dried or the joints where grout is

reapplied over wet joints will turn cloudy and must be removed and

dried before re-application. Please ASSURE there is NO WATER or

residual high HUMIDITY in the joints prior to grout. The presence of

WATER or high HUMIDITY may produce unexpected results including

the formation of Carbonation.

MIXING RATIO

COMPONENT A 100 parts in weight

COMPONENT B 8,3 parts in weight

The two components are pre-dosed in their respective packs within

the pail.

PACKS

5.5 pounds plastic bucket

11 pounds plastic bucket

PREPARING THE MIXTURE

Open the bucket and remove all the components (yellowish liquid

Component part B in the plastic pouch, instruction booklet and

separation disc) Part A is the premixed paste material in the

bottom of the bucket. Cut one corner of the plastic pouch (part B)

containing the hardening agent / catalyst, and pour it onto Part A

(paste). The 2 Components A and B are pre-packaged in the correct

mixing Ratio as indicated above. It is mandatory to pour out the entire

contents of the Component B, rolling and squeezing the plastic

pouch progressively from the sealed side towards the cut side.

Mix using an electric drill with the paddle at low speed until

achieving a smooth mixture without lumps. When the 2

components are properly mixed you will notice a homogeneous,

uniform paste without color variation. Scrape the sides and bottom

of the bucket with a spatula or trowel to ensure complete and proper

mixing. It is never advisable to mix by hand.

Do NOT OVERMIX! The paste will become hot and it will result in a

STARLIKE

CRYSTAL

TRANSLUCENT EPOXY MORTAR FOR GROUTING TRANSPARENT

AND ARTISTIC GLASS MOSAICS WITH JOINTS UP TO 1/8” (3.175 mm) WIDE

Summary of content (6 pages)

PAGE 1
Products to grout and clean ADESIVI CEMENTIZI STARLIKE® CRYSTAL TRANSLUCENT EPOXY MORTAR FOR GROUTING TRANSPARENT AND ARTISTIC GLASS MOSAICS WITH JOINTS UP TO 1/8” (3.175 mm) WIDE DESCRIPTION Part A consists of a mixture of epoxy resin, inert substances based on glass beads with a fine particle size and components of organic origin. Part B consists of a mixture of amine-based hardeners.
PAGE 2
Products to grout and clean ADESIVI CEMENTIZI shorter working time to apply the material before hardening, and will cause unwanted air into the mixture and can cause bubbling effect when applying GROUTING THE MOSAIC SURFACE Apply the mixture into the joints, using a suitable green epoxy float. Work the trowel to push the material in every cavity of the joint. Remove any excess using the same rubber float in a diagonal motion to the direction of the joints.
PAGE 3
Products to grout and clean ADESIVI CEMENTIZI If the white pad / felt and soft sponge becomes impregnated with resin and can no longer be cleaned, they should be replaced. Let the material harden completely without walking or using the area for at least 24 hours or longer based upon application temperature, see notes above. Do NOT COVER the grouted surface with any material, plastic, tarp, cloth or others for 24 – 48 hours under normal temperature conditions.
PAGE 4
Products to grout and clean ADESIVI CEMENTIZI IDENTIFICATION DATA Appearance Component A: translucent paste Component B: thick liquid Colour Crystal C.
PAGE 5
Products to grout and clean ADESIVI CEMENTIZI COVERAGE AREA with 1 BUCKET OF 5.
PAGE 6
Products to grout and clean ADESIVI CEMENTIZI CHEMICAL RESISTANCE TABLE (the table is a summary of the chemical resistance testing performed in accordance with UNI EN 12808 specifications CHEMICAL RESISTANCE OF installed STARLIKE® CRYSTAL grout Group Name Tannic Acid Tartaric Acid Oxalic Acid 2,5 5 37 10 2,5 5 10 25 50 1,5 50 96 10 10 10 Ammonia in solution Caustic Soda 25 50 Sodium Hypochlorite Conc.