Heat shrinkable cable end caps with spiral adhesive coating
Applications:
It is injection-molded with polyolefin and has UV and abrasion resistance. Hot melt adhesive is coated in a spiral shape
inside the tube, providing reliable waterproof and insulation protection for the cut surface of cables or air-filled cables.
Operating temperature range:
Continuous operating temperature: -55˚C~110˚C
Minimum shrink temperature: 80˚C
Full recovery temperature: Above 120˚C
Shrink ratio: 2:1
Can be easily installed on the cable end
Excellent abrasion resistance and mechanical protection
EVA hot melt adhesive coating
As supplied (mm)
After recovered (mm)
Cable diameter (mm)
H (min)
L (±10%)
H (±10%)
A (min)
W (±10%)
40
95
15 25 3.3 18-32
Property
Specification
Requirement
Test Method
Typical Value
Tensile strength
≥10.3MPa
ASTM D2671
≥14MPa
Elongation at break
≥200%
ASTM D2671
≥400%
Elongation at break after
aging
≥100%
ASTM D2671
(136˚C/168hrs)
≥300%
Dielectric strength
≥7.9kV/mm
ASTM D2671
15kV/mm
Volume resistivity
≥1014Ω‧cm
ASTM D2671
≥1014Ω‧cm