Exova Warringtonfire Holmesfield Road Warrington WA1 2DS United Kingdom T : +44 (0 1925 655116 F : +44 (0) 1925 655419 E : warrington@exova.com W: www.exova.com NF X 70–100-1: 2006 & NF X 70-100-2: 2006 Fire tests, Analysis of gaseous effluents. Part 1: Methods for analysing gases produced by thermal degradation. Part 2: Tubular furnace thermal degradation method. Date: 28th July 2017 Issue No.: 1 Page 1 A Report To: Weidmüller Interface GmbH & Co.
NF X 70–100-1: 2006 & NF X 70-100-2: 2006 Executive Summary Objective To determine the performance of the following product when tested in accordance with the procedure specified in NF X 70-100-1: 2006 & NF X 70-100-2: 2006. Generic Description Product reference Thickness Density Crosslinked ethylene vinyl “HSS-HF” & “HS-HF” 0.4-1mm 1.4g/ml³ acetate (EVA) heat shrink tubing Please see page 5 of this test report for the full description of the product tested Test Sponsor Weidmüller Interface GmbH & Co.
NF X 70–100-1: 2006 & NF X 70-100-2: 2006 Signatories Responsible Officer T. Mort * Senior Technical Officer Authorised S. Deeming * Business Unit Head * For and on behalf of Exova Warringtonfire. Report Issued: 28th July 2017 This version of the report has been produced from a .pdf format electronic file that has been provided by Exova Warringtonfire to the sponsor of the report and must only be reproduced in full.
NF X 70–100-1: 2006 & NF X 70-100-2: 2006 CONTENTS PAGE NO. EXECUTIVE SUMMARY ........................................................................................................................... 2 SIGNATORIES........................................................................................................................................... 3 TEST DETAILS ..........................................................................................................................................
NF X 70–100-1: 2006 & NF X 70-100-2: 2006 Test Details Purpose of test To determine the performance of specimens of a material when they are subjected to the conditions of test specified in NFX 70 - 100: 2006 “Analysis Of Gaseous effluents, Part 1: Methods for analysing gases produced by thermal degradation and Part 2: Tubular furnace thermal degradation method”.
NF X 70–100-1: 2006 & NF X 70-100-2: 2006 Description of Test Specimens The description of the specimens given below has been prepared from information provided by the original sponsor of the test. All values quoted are nominal, unless tolerances are given.
NF X 70–100-1: 2006 & NF X 70-100-2: 2006 Test Results Applicability of test results The test results relate only to the behaviour of the specimens of the product under the particular conditions of test; they are not intended to the sole criterion for assessing the potential smoke hazard of the product in use. The test results relate only to the specimens of the product in the form in which they were tested.
NF X 70–100-1: 2006 & NF X 70-100-2: 2006 Conclusion When tested in accordance with the procedure specified in NF X 70–100-1: 2006 & NF X 70-100-2: 2006 at a temperature of 600°C, the results obtained were • C.I.T calculated in accordance with NF F 16-101 (withdrawn) = 4.24 • R value calculated in accordance with BS 6853 Annex B.1(withdrawn) / LUL S1085 Attachment A.1 = 0.
NF X 70–100-1: 2006 & NF X 70-100-2: 2006 Table 1 GASES Concentration (mg/g) NF F 16-101 (withdrawn) reference values, ccl (mg/m3) BS 6853 (withdrawn) reference values, Fx (mg/g) (BS EN 45545-2) reference values, Ci (mg/m3) CIT (NF F 16-101 (withdrawn)) r value (BS 6853 Annex B.1 (withdrawn)) CITNLP (BS EN 455452) CARBON MONOXIDE 53.04 1750 280 1380 3.03 0.19 0.04 CARBON DIOXIDE 679.80 90000 14000 72000 0.76 0.05 0.01 HYDROGEN CHLORIDE 0.36 150 15 75 0.24 0.02 0.
NF X 70–100-1: 2006 & NF X 70-100-2: 2006 Observations In the case of each specimen the test duration was 40 minutes and the volume of the gas sampled was 80 litres. In each case the air was circulated using a suction method. In the case of each specimen a nominally 1g sample was obtained which was representative of the substance or material as used in practice. Specimen No.
NF X 70–100-1: 2006 & NF X 70-100-2: 2006 Revision History Issue No : Issue Date: Revised By: Approved By: Reason for Revision: Document No.: Author: Client: Additional Test Report 386712 T. Mort Page No.: 11 of 11 Issue Date: 28th July 2017 Weidmüller Interface GmbH & Co. KG Issue No.